BV EH32 steel plate,BV Grade EH32 shipbuilding steel price,BV Grade EH32 steel supplier and manufacturer.
BV EH32 shipbuilding Steel Description:
All BV steels are standard carbon steels. As with other grades of steel, they have a specific gravity of 7.8.Higher-strength BV shipbuilding steel comes in six grades of two strengths, The BV EH 32 grade steel plates have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa).
BV EH32 Shipbuilding Steel Application:
BV EH32 Shipbuilding steel plates are suitable for container and bulk cargo vessels as well as cruise ships, ferries and yachts.
BV EH32 Steel Grade Specification:
Thickness: 4mm to 260mm,
Width: 1200mm to 4000mm
Length: 3000mm to 18000mm.
BV EH32 Ship Steel Delivery Conditions:
BV EH32 Delivery Condition: AR(As hot rolled only), TMCP, Q+T(Quenching+Tempering), N(Normalizing),CR( Control rolled only)
BV EH32 Steel Plate Additional Service:
Hot rolled(HR), control rolled(CR) Thermo Mechanical Control Process(TMCP), Normalized , Q&T, impact test, Z15,Z25,Z35.
BV EH32 Shipbuilding Steel Chemical Composition:
|
Grade |
C % |
Si % |
Mn % |
P % |
S % |
V % |
AL % |
Cr % |
|
BV Grade EH32 |
0.180 |
0.1-0.5 |
0.90-1.6 |
0.035 |
0.035 |
0.05-0.10 |
0.015 |
0.200 |
|
Cu % |
Mo % |
Nb % |
Ni % |
Ti % |
|
|
|
|
|
0.350 |
0.080 |
0.02-0.05 |
0.400 |
0.020 |
|
|
|
BV EH32 Grade Ship Steel Mechanical Properties:
| Grade |
Thickness(mm) |
MinYield(Mpa) |
Tensile(Mpa) |
Elongation (%) |
Min Impact Energy |
|
|
BV Grade EH32 |
8mm-50mm |
Min 315Mpa |
440-590Mpa |
22 |
-40 |
34J |
|
51mm-70mm |
Min 315Mpa |
440-590Mpa |
22 |
-40 |
38J |
|
|
71mm-100mm |
Min 315Mpa |
440-590Mpa |
22 |
-40 |
46J |
|
|
The minimum impact energy is longitudinal energy |
||||||
BEBON BV EH32 shipbuilding steel plates and sheets have been exported to worldwide shipyard and ship building company,we have mill BV Grade EH32 for shipbuilding.If you have any needs in BV Grade EH32 steel plate price and suppliers, please feel free to contact us.