Aug-15-2025
Material Characteristics
Cold rolled 316 stainless steel BA 8K mirror plate is based on 316L austenitic stainless steel. After cold rolling, it undergoes a BA (bright annealing) treatment. The surface undergoes multiple precision grinding and polishing s
Aug-15-2025
Material Characteristics
SUS 316 stainless steel plate, with its alloy ratio of 18% chromium, 10-14% nickel, and 2.5% molybdenum, exhibits excellent corrosion resistance in architectural decoration, particularly suitable for coastal environments with hig
Aug-15-2025
As a benchmark material for austenitic stainless steel, ASTM 316 No.4 forms a unique hairline finish through surface drawing technology, combining functionality and decorative value. Its molybdenum content reaches 2% -3%, significantly improving its resis
Aug-15-2025
ASTM A572 grade 50 HR steel coil, a high-strength, low-alloy structural steel, combines excellent mechanical properties with processing characteristics. Its minimum yield strength reaches 50 ksi (345 MPa), and its uniform microstructure is achieved throug
Aug-08-2025
ASTM A572 grade 50 hot rolled carbon steel plate adopts niobium vanadium microalloying design, with a yield strength of ≥ 345MPa, combining high strength and good plasticity. Its hot rolling process ensures that the thickness tolerance is controlle
Aug-08-2025
ASTM A572 grade 50 hot rolled steel coil core features
Niobium vanadium microalloy (Mn ≤ 1.35%), yield strength ≥ 345MPa, hot-rolled coil thickness 0.5-12mm, with both high strength and excellent cold bending performance. Suitable for stamp
Aug-08-2025
ASTM A572 grades classification characteristics
Micro alloys containing niobium vanadium (C ≤ 0.23%) are classified into five grades based on yield strength: Gr42 (290MPa), Gr50 (345MPa), Gr55 (380MPa), Gr60 (415MPa), and Gr65 (450MPa), with tensi
Aug-08-2025
ASTM A572 grade 50 low alloy steel plates core features
Niobium vanadium microalloy (C ≤ 0.23%), yield strength ≥ 345MPa, tensile strength 490-600MPa, elongation 22% -35%. Hot rolled/normalized delivery, combining high strength and excellen
Aug-08-2025
ASTM A572 grade 50 mild steel plate material characteristics
ASTM A572 grade 50 is a typical niobium vanadium microalloyed structural steel in the American standard. Its mechanical properties are as follows: yield strength ≥ 345MPa, tensile streng
Aug-01-2025
ASTM A572 grade 50 is a high-strength low-alloy hot rolled steel coil with a yield strength of ≥ 345MPa, a carbon content of ≤ 0.20%, and the addition of niobium element (0.005% -0.05%). The balance between strength and toughness is achieved
Aug-01-2025
As an important base for the global steel industry, China has multiple high-quality enterprises specializing in supplying ASTM A572 grade 50 carbon steel plates. Steel mills represented by BBN use niobium vanadium alloying technology to produce steel plat
Aug-01-2025
A572 grade 50 structural steel material properties
A572 grade 50 belongs to low-alloy high-strength structural steel, with a yield strength of 345MPa (50ksi) and excellent weldability and formability. The chemical composition of A572 grade 50 has a carbo
Aug-01-2025
ASTM A572 grade 50 hot rolled steel coil belongs to high strength low alloy structural steel, produced by hot rolling process. Its chemical composition strictly controls the carbon content (C ≤ 0.23%) and sulfur phosphorus impurities (≤ 0.05
Aug-01-2025
ASTM A572 grade 50 carbon structural steel, as a representative of American high strength low alloy steel, has a yield strength of 345MPa (50ksi) and excellent weldability and formability. Fine grain strengthening is achieved by adding microalloying eleme
Jul-25-2025
ASTM A36 hot-rolled structural steel plate is the most commonly used low-carbon steel material in the construction field, with a carbon content controlled in the range of 0.25-0.29%. A36 steel plate is produced through a high-temperature rolling process,