17Cr16Ni2 GB/T4237 Martensite stainless steel plate/coil

17Cr16Ni2 GB/T4237 Martensite stainless steel plate/coil Chemical Composition and Mechanical Property

Grade	C	Si	Mn	P	S	Ni	Cr	Mo	Cu	N	Other
17Cr16Ni2	0.12 - 0.20	1.00	1.00	0.025	0.015	2.00 - 3.00	15.00 ~ 18.00	---	---	---	---

Grade	Non-proportional extension strength, R_p0.2/MPa ≥	Tensile strength, R_m/MPa ≥	Elongation, A/% ≥	Cold-formed 180° d : Apex diameter a : Plate thickness	Hardness
Grade	Non-proportional extension strength, R_p0.2/MPa ≥	Tensile strength, R_m/MPa ≥	Elongation, A/% ≥	Cold-formed 180° d : Apex diameter a : Plate thickness	HBW ≤	HRB ≤	HV ≤
17Cr16Ni2	690	880 - 1080	12	---	262 - 326	---	---
17Cr16Ni2	1050	1350	10	---	388	---	---

17Cr16Ni2 GB/T4237 Martensite stainless steel plate/coil Application

17Cr16Ni2 stainless steel plate/coil is commonly used for produce high resistance to corrosive nitric acid and organic acid components, containers and equipment.

17Cr16Ni2 GB/T4237 Martensite stainless steel plate/coil Other Name

GB/T4237 17Cr16Ni2 stainless steel plate, Martensite 17Cr16Ni2 stainless steel coil

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support