ASTM A514/A514M Grade H Carbon and Low-alloy High-strength Steel Coil
ASTM A514/A514M Grade H Carbon and Low-alloy High-strength Steel Coil Chemical Composition and Mechanical Property
| Element | Content (%) |
| Iron, Fe | 97 |
| Nickel, Ni | 0.85 |
| Manganese, Mn | 0.8 |
| Molybdenum, Mo | 0.5 |
| Chromium, Cr | 0.48 |
| Copper, Cu | 0.33 |
| Silicon, Si | 0.25 |
| Carbon, C | 0.10 - 0.20 |
| Vanadium, V | 0.06 |
| Boron, B | 0.003 |
| Tensile strength, ultimate | 760 - 895 MPa | 110000 - 130000 psi |
| Tensile strength, yield (@0.200%) | 690 MPa | 100000 psi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 18% | 18% |
ASTM A514/A514M Grade H Carbon and Low-alloy High-strength Steel Coil Application
A514/A514M Grade H is used in Construction of Bridges, Highway Construction and Other Engineering construction.
ASTM A514/A514M Grade H Carbon and Low-alloy High-strength Steel Coil Other Name
ASTM A514/A514M Low-alloy High-strength Steel, A514/A514M Grade H carbon steel coil, A514/A514M Grade H Low-alloy High-strength Steel Coil
Additional Condition
UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.
Other Terms
Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.
Sales Department Team
Send Order Request Online Chat