Home > steel coil > Hot rolled steel coil for automobile frame > Q/BQB 310-2009 or JIS G 3113-2006

Q/BQB 310-2009 or JIS G3113-2006 SAPH400 Hot Rolled Steel Coil

Q/BQB 310-2009 or JIS G3113-2006 SAPH400 Hot Rolled Steel Coil Chemical Composition and Mechanical Property

C max

Si max.

Mn max.

P max.

S max.

Alt min.

0.21

0.30

1.40

0.030

0.025

0.010

Yield Strength (MPa) min.

Tensile Strength (MPa) min.

Elongation % min.

Thickness(mm)

Thickness(mm)

t<6.0

6≤t<8.0

8.0≤t≤25.4

400

1.6≤t<2.0

2.0≤t<2.5

2.5≤t<t3.15

3.15≤t<4.0 4.0≤t<6.3

6.3≤t≤25.4

255

235

235

31

32

34

 35  36

37

Q/BQB 310-2009 or JIS G3113-2006 SAPH400 Hot Rolled Steel Coil Application

Q/BQB 310-2009 or JIS G3113-2006 SAPH400 hot rolled steel coil is mainly for Automobile frames, beams, roll-type wheels, automotive transmission pipe, automobile axle housing and so on.

Q/BQB 310-2009 or JIS G3113-2006 SAPH400 Hot Rolled Steel Coil Other Name

JIS G3113-2006 SAPH400 hot rolled steel coil, Q/BQB 310-2009 SAPH400 hot rolled steel coil

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.