Q235B + 304 Clad steel plate

Q235B + 304 Clad steel plate Chemical Composition and Mechanical Property

Grade	C %	Si %	Mn %	P %	S %
Q235B	0.22	0.35	1.4	0.045	0.045

Grade	Thickness(mm)	Yield Strength (Mpa)	Tensile Strength	Elongation(%)	Min Impact Energy
Grade	Thickness(mm)	Yield Strength (Mpa)	(MPa)	Elongation(%)	Min Impact Energy
Q235B	≤ 16	235	370-500	26	20	27J
	> 16-40	225	370-500	25	20	27J
	>40	215	370-500	24	20	27J
The min impact energy is longitudinal energy

Grade

Cooper

304(S30400)

0.07

2.0

0.045

0.030

0.75

17.5-19.5

8.0-10.5

0.10

Grade

Yield strength

(N/mm2), min

Tensile strength (N/mm2), min

Elongation in 2 in. (50mm), %, min

Hardness, max
Brinell	Rockwell B

Cold bend

Austenitic (Chromium-Nickel) (Chromium-Manganese-Nickel)

304(S30400)

205

515

201

not required

Q235B + 304 Clad steel plate Application

Q235B + 304 Clad steel plates are used in Construction of Bridges, Highway Construction and Other Engineering construction.

Q235B + 304 Clad steel plate Other Name

Q235B + 304 Clad steel plate, Q235B steel plate, 304 steel plate

Additional Condition

UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

Other Terms

Packaging Details: Standard export seaworthy packing or as required.
Delivery Time: 30-50 days, 7 days for stock goods.
Loading Port: Shanghai ,Tianjin, Qingdao.
Offer Ability:5 000MT/Per Month.
MOQ: 1 Pcs.

Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service 24h Technical support